Copper Strip find many applications as Electrical Conductors, Switch Terminals, Hardware used in Electrical Circuits, Electrical Contacts.
These copper strip products are available in Hard, Half-hard and Soft condition.

Material with minimum copper content of 99.9% as per IS 191:

Material with minimum copper content of 99.9% as per IS 191 & IS 1897 copper silver/copper nickel:

Square Edge, Radius Edge, Full Radius Edge.
Length: Up to 6400mm (21`) (depending on section) with standard overall cutting tolerance of 100mm.

Our Copper Flat Bar can be Electro-plated with Tin or Silver.

BUSBAR

All of our copper sheets are 99.9% pure copper (premium alloy 110) annealed (dead soft) with a smooth commercial finish.

Chemical Composition Of Copper
Material	Normal Composition	Nearest Relevant Composition Specification
		BS: 2870	ISO	JIS
Electrolytic Tough Pitch H.C. Copper	Cu - 99.90% Min.	C 101	Cu ETP	H 3100
	Pb - 0.005% Max		1337	C 1100
	Bi - 0.001% Max
	O2-0.060% Max
Phosphorous Deoxidized Copper(DONA)	Cu - 99.85% Min.	C106	Cu DHP	H 3100
Phosphorous Deoxidized Copper(DONA)	P-0.013-0.050%	C106	1337	C 1220
* Material confirming to other National Specification e.g. ASTM, DIN etc. is also provided.
* Available in Strips, Sheets, Plates & Circles form.

COPPER
TYPICAL MECHANICAL PROPERTIES AS PER : B.S. : 2870
Material	Temper	Tensile Strength N/mm2	Elongation% on 50 mm G.L.	Vickers Hardness	ISO	JIS
Material	Temper	Tensile Strength N/mm2	Elongation% on 50 mm G.L.	VPN	ISO	JIS
Electrolytic	'O'	210 Min	35 Min	55 Max	Cu ETP	H 3100
Tough Pitch H.C. Copper	M	210 Min	35 Min	65 Max	ISO : 1337	C 1100
	1/2 H	240 Min	10 Min	70 to 95
	H	290 Min	-	90 Min
Phosphorous	'O'	210 Min	35 Min	55 Max	Cu DHP	H 3100
Deoxidized Copper	M	210 Min	35 Min	65 Max	ISO : 1337	C 1220
	1/2 H	240 Min	10 Min	70 to 95
	H	290 Min	-	90 Min
'O'b :	Annealed Condition.
1/2Hv:	Half Hard
Hb:	Hard
* :	Electric Conductivity at 20 Deg. Cel. 100% IACS(For Cu ETP 'O'Temper)